This all makes sense. Does anyone have any examples from the literature of VO2 grown on quartz and/or aluminum that would give me an idea on their respective resistivity values? I am having a hard time finding some literature on that topic.
Well the transition is induced by temperature and I know that resistivity is a function of temperature. However, resistivity is only a material specific property and since what we are depositing is still only VO2 and I am thinking the structure will be the same (no matter if we use quartz or...
I am depositing VO2 thin films on quartz and aluminum substrates and I need to find out whether the choice of substrate can effect the resistivity of the VO2 film. I know resistivity is a function of temperature but am not sure if it is effected by substrate choice. Any thoughts?